Effect of mixed pinning landscapes produced by 6MeV oxygen irradiation on the resulting critical current densities Jc in 1.3µm thick GdBa2Cu3O7-d coated conductors grown by co-evaporation
Fil: Haberkorn, N. Comisión Nacional de Energía Atómica. Instituto Balseiro; Argentina; Universidad Nacional de Cuyo; Argentina; Consejo Nacional de Investigaciones Científicas y Técnicas
Saved in:
| Main Authors: | , , , , , , , , |
|---|---|
| Other Authors: | |
| Language: | English |
| Published: |
Elsevier
2017
|
| Subjects: | |
| Online Access: | https://nuclea.cnea.gob.ar/handle/20.500.12553/5270 |
| Tags: |
No Tags, Be the first to tag this record!
|
Similar Items: Effect of mixed pinning landscapes produced by 6MeV oxygen irradiation on the resulting critical current densities Jc in 1.3µm thick GdBa2Cu3O7-d coated conductors grown by co-evaporation
- Strong influence of the oxygen stoichiometry on the vortex bundle size and critical current densities J c of GdBa2Cu3Ox -coated conductors grown by co-evaporation
- Anomalous reduction in the long-time flux creep relaxation in superconducting Ca10(Pt4As8)((Fe1−x Ptx )2As2)5 (x ≈ 0.05) single crystals
- Influence of random point defects introduced by proton irradiation on the flux creep rates and magnetic field dependence of the critical current density Jc of co-evaporated GdBa2Cu3O7−δ coated conductors
- In-field dependences of the critical current density Jc in GdBa2Cu3O7-d coated conductors produced by Zr irradiation and post-annealing at low temperatures
- Thickness dependence of the superconducting properties of Y- Mo2N thin films on Si (001) grown by DC sputtering at room temperature
- Smooth surfaces in very thin GdBa2Cu3O7δfilms for application in superconducting tunnel junctions